ENAW-AlMg1Si0.8CuMn
آلومینیوم کارشده
خلاصه مشخصات
چگالی-g/cm³
مدول الاستیسیتهناموجود
استحکام کششیناموجود
استحکام تسلیمناموجود
سختی برینلناموجود
حداکثر دمای کاریناموجود
ترکیب شیمیایی
SI
ENAW-AlMg1Si0.8CuMn ( ENAW-6013 ) Aluminium - 6000 series ( Magnesium Mg and Silicon Si are major alloying elements ) Chemical composition. Equivalents of ENAW-AlMg1Si0.8CuMn ( ENAW-6013 ). Standards.1 Mechanical Properties. Hardness%
سایر خواص
کد وضعیت F
Fabricated (as cast)
کد وضعیت H
Strain hardened
کد وضعیت O
Annealed
کد وضعیت T
Thermally treated to produce stable tempers other than F, O or H
کد وضعیت T1
Cooled from an elevated temperature shaping process and naturally aged
کد وضعیت T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
کد وضعیت T3
Solution heat treated, cold worked and naturally aged
کد وضعیت T4
Solution heat treated and naturally aged
کد وضعیت T5
Cooled from an elevated temperature shaping process and then artificially aged
کد وضعیت T6
Solution heat treated and then artificially aged
کد وضعیت T7
Solution heat treated and then artificially overaged (stabilised)
کد وضعیت T8
Solution heat treated, cold worked and then artificially aged
کد وضعیت T9
Solution heat treated, artificially aged and then cold worked
کد وضعیت W
Solution heat treated (unstable temper)
نامها و معادلهای ثبتشده
ENAW-6013ENAW-AlMg1Si0.8CuMn
استانداردها
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products