AWS E309Mo (W30920) Weld Metal
Austenitic & General Stainless Steels
Property Overview
Density7.9g/cm³
Elastic Modulus200GPa
Tensile Strength620MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.12%
CR
22 to 25%
NI
12 to 14%
MO
2.0 to 3.0%
MN
0.5 to 2.5%
SI
0 to 1.0%
P
0 to 0.040%
S
0 to 0.030%
CU
0 to 0.75%
FE
53.6 to 63.5%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
34 %
Poisson's Ratio
0.28
Shear Modulus
79 GPa
Tensile Strength: Ultimate (UTS)
620 MPa
Physical
Density
7.9 g/cm 3
Thermal
Latent Heat of Fusion
300 J/g
Melting Completion (Liquidus)
1430 °C
Melting Onset (Solidus)
1390 °C
Specific Heat Capacity
480 J/kg-K
Thermal Conductivity
15 W/m-K
Thermal Diffusivity
3.9 mm 2 /s
Thermal Expansion
14 µm/m-K
Thermal Shock Resistance
15 points
Electrical
Electrical Conductivity: Equal Volume
2.1 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.4 % IACS
Calculated
PREN (Pitting Resistance)
32
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
22 points
Strength to Weight: Bending
20 points
Environmental
Base Metal Price
22 % relative
Embodied Carbon
4.2 kg CO 2 /kg material
Embodied Energy
59 MJ/kg
Embodied Energy
59 MJ/kg 25 x 10 3 BTU/lb
Embodied Water
180 L/kg
Embodied Water
180 L/kg 22 gal/lb
Registered Designations & Aliases
AWS E309Mo (W30920) Weld MetalW30920