AWS E219 (W32310) Weld Metal
Austenitic & General Stainless Steels
Property Overview
Density7.7g/cm³
Elastic Modulus200GPa
Tensile Strength690MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.060%
CR
19 to 21.5%
NI
5.5 to 7.0%
MO
0 to 0.75%
MN
8.0 to 10%
SI
0 to 1.0%
N
0.1 to 0.3%
P
0 to 0.040%
S
0 to 0.030%
CU
0 to 0.75%
FE
58.6 to 67.4%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
17 %
Poisson's Ratio
0.28
Shear Modulus
78 GPa
Tensile Strength: Ultimate (UTS)
690 MPa
Physical
Density
7.7 g/cm 3
Thermal
Latent Heat of Fusion
290 J/g
Melting Completion (Liquidus)
1400 °C
Melting Onset (Solidus)
1360 °C
Specific Heat Capacity
480 J/kg-K
Thermal Conductivity
14 W/m-K
Thermal Diffusivity
3.8 mm 2 /s
Thermal Expansion
15 µm/m-K
Thermal Shock Resistance
17 points
Calculated
PREN (Pitting Resistance)
25
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
23 points
Environmental
Base Metal Price
15 % relative
Embodied Carbon
3.1 kg CO 2 /kg material
Embodied Energy
44 MJ/kg
Embodied Energy
44 MJ/kg 19 x 10 3 BTU/lb
Embodied Water
160 L/kg
Embodied Water
160 L/kg 19 gal/lb
Registered Designations & Aliases
AWS E219 (W32310) Weld MetalW32310