AWS E209 (W32210) Weld Metal
Austenitic & General Stainless Steels
Property Overview
Density7.8g/cm³
Elastic Modulus200GPa
Tensile Strength770MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 0.060%
CR
20.5 to 24%
NI
9.5 to 12%
MO
1.5 to 3.0%
MN
4.0 to 7.0%
SI
0 to 1.0%
N
0.1 to 0.3%
P
0 to 0.040%
S
0 to 0.030%
CU
0 to 0.75%
V
0.1 to 0.3%
FE
51.5 to 64.3%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
17 %
Poisson's Ratio
0.28
Shear Modulus
79 GPa
Tensile Strength: Ultimate (UTS)
770 MPa
Physical
Density
7.8 g/cm 3
Thermal
Latent Heat of Fusion
300 J/g
Melting Completion (Liquidus)
1420 °C
Melting Onset (Solidus)
1370 °C
Specific Heat Capacity
480 J/kg-K
Thermal Expansion
14 µm/m-K
Thermal Shock Resistance
19 points
Calculated
PREN (Pitting Resistance)
33
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
28 points
Strength to Weight: Bending
24 points
Environmental
Base Metal Price
21 % relative
Embodied Carbon
4.4 kg CO 2 /kg material
Embodied Energy
63 MJ/kg
Embodied Energy
63 MJ/kg 27 x 10 3 BTU/lb
Embodied Water
180 L/kg
Embodied Water
180 L/kg 22 gal/lb
Registered Designations & Aliases
AWS E209 (W32210) Weld MetalW32210