1100 (Al99.0Cu, A91100) Aluminum

Alloy Steels

Material conditionannealed

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density2.7g/cm³

Elastic Modulus69GPa

Tensile Strength88MPa

Yield Strength29MPa

Brinell Hardness23HB

Maximum Service Temperature180°C

Weight Calculator

Chemical Composition

0 to 0.050%

0 to 1.0%

0.050 to 0.2%

99 to 99.95%

RES.

Residuals res. | | 0 to 0.15%

RESIDUALS RES.

0 to 0.15%

0 to 0.1%

0 to 1.0%

Mechanical

Elastic (Young's, Tensile) Modulus

69 GPa

Elongation at Break

32 %

Fatigue Strength

35 MPa

Poisson's Ratio

0.33

Shear Modulus

26 GPa

Shear Strength

61 MPa

Tensile Strength: Ultimate (UTS)

88 MPa

Tensile Strength: Yield (Proof)

29 MPa

Hardness

Brinell Hardness

Physical

Density

2.7 g/cm 3

Thermal

Latent Heat of Fusion

400 J/g

Maximum Temperature: Mechanical

180 °C

Melting Completion (Liquidus)

660 °C

Melting Onset (Solidus)

640 °C

Specific Heat Capacity

900 J/kg-K

Thermal Conductivity

220 W/m-K

Thermal Diffusivity

90 mm 2 /s

Thermal Expansion

24 µm/m-K

Thermal Shock Resistance

3.9 points

Electrical

Electrical Conductivity: Equal Volume

59 % IACS

Electrical Conductivity: Equal Weight (Specific)

190 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

22 MJ/m 3

Resilience: Unit (Modulus of Resilience)

6.1 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

50 points

Strength to Weight: Axial

9.0 points

Strength to Weight: Bending

16 points

Environmental

Base Metal Price

9.0 % relative

Embodied Carbon

8.2 kg CO 2 /kg material

Embodied Energy

150 MJ/kg

Embodied Energy

150 MJ/kg 66 x 10 3 BTU/lb

Embodied Water

1190 L/kg

Embodied Water

1190 L/kg 140 gal/lb

Physical Other

Calomel Potential

-740 mV

Registered Designations & Aliases

1100 (Al99.0Cu, A91100) AluminumA91100Al1100Al99.0CuAl99.0CuEN AW-1100

Standards

ASTM B209 ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate

ASTM B210 ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes

ASTM B211 ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire

ASTM B221 ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes

ASTM B247 ASTM B247: Standard Specification for Aluminum and Aluminum-Alloy Die Forgings, Hand Forgings, and Rolled Ring Forgings

ASTM B483 ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications

ASTM B491 ASTM B491: Standard Specification for Aluminum and Aluminum-Alloy Extruded Round Tubes for General-Purpose Applications

ASTM B491 ASTM B491: Standard Specification for Aluminum and Aluminum-Alloy Extruded Round Tubes for General-Purpose Applications ASTM B247: Standard Specification for Aluminum and Aluminum-Alloy Die Forgings, Hand Forgings, and Rolled Ring Forgings ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes Environmental Degradation of Advanced and Traditional Engineering Materials, Lloyd H. Hihara et al., 2014. ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate Aluminum Standards and Data, Aluminum Association Inc., 2013

ASTM B547 ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube

ISO 18273 ISO 18273: 2004 Welding consumables. Wire electrodes, wires and rods for welding of aluminium and aluminium alloys.