EN 1.0558 (GE300) Cast Non-Alloy Steel
Other Steels
Property Overview
Density7.9g/cm³
Elastic Modulus190GPa
Tensile Strength640MPa
Yield Strength340MPa
Brinell HardnessUnknown
Maximum Service Temperature400°C
Chemical Composition
P
0 to 0.035%
S
0 to 0.030%
FE
99.935 to 100%
Mechanical
A - Min. elongation at fracture (%) (+N)
15-18
+N
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
18 %
Fatigue Strength
230 MPa
Impact Strength: V-Notched Charpy
33 J
Poisson's Ratio
0.29
Shear Modulus
73 GPa
Tensile Strength: Ultimate (UTS)
640 MPa
Tensile Strength: Yield (Proof)
340 MPa
Physical
Density
7.9 g/cm 3
Thermal
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C
Melting Completion (Liquidus)
1470 °C
Melting Onset (Solidus)
1430 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
53 W/m-K
Thermal Diffusivity
14 mm 2 /s
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
20 points
Electrical
Electrical Conductivity: Equal Volume
7.8 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.9 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
99 MJ/m 3
Resilience: Unit (Modulus of Resilience)
300 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
22 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
1.7 % relative
Embodied Carbon
1.4 kg CO 2 /kg material
Embodied Energy
18 MJ/kg
Embodied Energy
18 MJ/kg 7.7 x 10 3 BTU/lb
Embodied Water
45 L/kg
Embodied Water
45 L/kg 5.3 gal/lb
Registered Designations & Aliases
1.05581.0558EN 1.0558 (GE300) Cast Non-Alloy SteelGE300GE300
Standards
EN 10293 EN 10293: 2005 Steel castings for general engineering uses
EN 10293 EN 10293: Steel castings - Steel castings for general engineering uses