EN 1.5410 (G10MnMoV6-3) Cast Steel
Other Steels
quenched and tempered
Property Overview
Density7.8g/cm³
Elastic Modulus190GPa
Tensile Strength560MPa
Yield Strength400MPa
Brinell Hardness170HB
Maximum Service Temperature400°C
Chemical Composition
C
0 to 0.12%
MO
0.2 to 0.4%
MN
1.2 to 1.8%
SI
0 to 0.6%
P
0 to 0.025%
S
0 to 0.020%
V
0.050 to 0.1%
FE
96.9 to 98.6%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Elongation at Break
24 %
Fatigue Strength
290 MPa
Impact Strength: V-Notched Charpy
67 J
Poisson's Ratio
0.29
Shear Modulus
73 GPa
Tensile Strength: Ultimate (UTS)
560 MPa
Tensile Strength: Yield (Proof)
400 MPa
Hardness
Brinell Hardness
170
Physical
Density
7.8 g/cm 3
Thermal
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C
Melting Completion (Liquidus)
1460 °C
Melting Onset (Solidus)
1420 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
51 W/m-K
Thermal Diffusivity
14 mm 2 /s
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
16 points
Electrical
Electrical Conductivity: Equal Volume
7.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.3 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
120 MJ/m 3
Resilience: Unit (Modulus of Resilience)
430 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
19 points
Environmental
Base Metal Price
2.3 % relative
Embodied Carbon
1.7 kg CO 2 /kg material
Embodied Energy
22 MJ/kg
Embodied Energy
22 MJ/kg 9.6 x 10 3 BTU/lb
Embodied Water
49 L/kg
Embodied Water
49 L/kg 5.8 gal/lb
Registered Designations & Aliases
1.54101.5410EN 1.5410 (G10MnMoV6-3) Cast SteelG10MnMoV6-3G10MnMoV6-3
Standards
EN 10293 EN 10293: 2005 Steel castings for general engineering uses
EN 10293 EN 10293: Steel castings - Steel castings for general engineering uses
EN 10293 EN 10293: Steel castings - Steel castings for general engineering uses Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993 Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
EN 10340 EN 10340: 2007 Steel castings for structural uses