UNS Z21210 (Zn-0.08Pb) Rolled Zinc

Zinc Alloys

Material conditionhot worked

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density7.1g/cm³

Elastic ModulusUnknown

Tensile Strength150MPa

Yield StrengthUnknown

Brinell Hardness42HB

Maximum Service TemperatureUnknown

Weight Calculator

Chemical Composition

Mechanical

Elongation at Break

58 %

Fatigue Strength

29 MPa

Tensile Strength: Ultimate (UTS)

150 MPa

Hardness

Brinell Hardness

Rockwell B Hardness

Physical

Density

7.1 g/cm 3

Thermal

Melting Completion (Liquidus)

420 °C

Melting Onset (Solidus)

420 °C

Specific Heat Capacity

400 J/kg-K

Thermal Conductivity

110 W/m-K

Thermal Diffusivity

38 mm 2 /s

Thermal Expansion

32 µm/m-K

Electrical

Electrical Conductivity: Equal Volume

28 % IACS

Electrical Conductivity: Equal Weight (Specific)

35 % IACS

Calculated

Strength to Weight: Axial

5.7 points

Strength to Weight: Bending

8.6 points

Registered Designations & Aliases

UNS Z21210 (Zn-0.08Pb) Rolled ZincZ21210Zn-0.08Pb