EN-GJMW-400-5
Cast Iron
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile StrengthUnknown
Yield Strength200MPa
Brinell Hardness220HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%)
12
A - Min. elongation at fracture (%)
8
A - Min. elongation at fracture (%)
5
A - Min. elongation at fracture (%)
4
R p0.2 0.2% proof strength (MPa)
200
R p0.2 0.2% proof strength (MPa)
220
R p0.2 0.2% proof strength (MPa)
230
Hardness
Brinell hardness (HB):
220
Other
Nominal diameter (mm):
to 6
Nominal diameter (mm):
6 - 9
Nominal diameter (mm):
9 - 12
Nominal diameter (mm):
12 - 15
Nominal diameter(mm):
to 9
Registered Designations & Aliases
EN-GJMW-400-5EN-JM1030
Standards
EN 1562 EN 1562: 1997 Founding. Malleable cast irons