EN-GJMW-360-12
Cast Iron
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile StrengthUnknown
Yield Strength170MPa
Brinell Hardness200HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%)
16
A - Min. elongation at fracture (%)
15
A - Min. elongation at fracture (%)
12
A - Min. elongation at fracture (%)
7
R p0.2 0.2% proof strength (MPa)
170
R p0.2 0.2% proof strength (MPa)
190
R p0.2 0.2% proof strength (MPa)
200
Hardness
Brinell hardness (HB):
200
Other
Nominal diameter (mm):
to 6
Nominal diameter (mm):
6 - 9
Nominal diameter (mm):
9 - 12
Nominal diameter (mm):
12 - 15
Nominal diameter(mm):
to 9
Registered Designations & Aliases
EN-GJMW-360-12EN-JM1020
Standards
EN 1562 EN 1562: 1997 Founding. Malleable cast irons