UNS C15500 Silver-Bearing Copper
Copper Alloys
O50 (light annealed)
Property Overview
Density8.9g/cm³
Elastic Modulus120GPa
Tensile Strength280MPa
Yield Strength130MPa
Brinell HardnessUnknown
Maximum Service Temperature200°C
Chemical Composition
P
0.040 to 0.080%
CU
99.75 to 99.853%
AG
0.027 to 0.1%
MG
0.080 to 0.13%
RES.
Residuals res. | | 0 to 0.2%
RESIDUALS RES.
0 to 0.2%
Mechanical
Elastic (Young's, Tensile) Modulus
120 GPa
Elongation at Break
37 %
Fatigue Strength
100 MPa
Poisson's Ratio
0.34
Shear Modulus
43 GPa
Shear Strength
190 MPa
Tensile Strength: Ultimate (UTS)
280 MPa
Tensile Strength: Yield (Proof)
130 MPa
Hardness
Rockwell F Hardness
70
Physical
Density
8.9 g/cm 3
Thermal
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C
Melting Completion (Liquidus)
1080 °C
Melting Onset (Solidus)
1080 °C
Specific Heat Capacity
390 J/kg-K
Thermal Conductivity
350 W/m-K
Thermal Diffusivity
100 mm 2 /s
Thermal Expansion
17 µm/m-K
Thermal Shock Resistance
9.8 points
Electrical
Electrical Conductivity: Equal Volume
90 % IACS
Electrical Conductivity: Equal Weight (Specific)
91 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
84 MJ/m 3
Resilience: Unit (Modulus of Resilience)
72 kJ/m 3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
8.6 points
Strength to Weight: Bending
11 points
Environmental
Base Metal Price
33 % relative
Embodied Carbon
2.7 kg CO 2 /kg material
Embodied Energy
42 MJ/kg
Embodied Energy
42 MJ/kg 18 x 10 3 BTU/lb
Embodied Water
360 L/kg
Embodied Water
360 L/kg 43 gal/lb
Registered Designations & Aliases
C15500UNS C15500 Silver-Bearing Copper