Magnesium Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength250MPa
Yield Strength170MPa
Brinell Hardness80 - 90HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (T6), (S)
2
R p0.2 0.2% proof strength (MPa) (T6), (S)
170
Rm - Tensile strength (MPa) (T6), (S)
250
Hardness
Brinell hardness (HB): (T6), (S)
80 - 90
Registered Designations & Aliases
EN-MC95310EN-MCMgY5RE4Zr
Standards
EN 1753 EN 1753: 1997 Magnesium and magnesium alloys. Magnesium alloy ingots and castings