EN-MCMgRE3Zn2Zr
Magnesium Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength145MPa
Yield Strength100MPa
Brinell Hardness50 - 60HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (T5), (K)
3
A - Min. elongation at fracture (%) (T5), (S)
2.5
R p0.2 0.2% proof strength (MPa) (T5), (K)
100
R p0.2 0.2% proof strength (MPa) (T5), (S)
95
Rm - Tensile strength (MPa) (T5), (K)
145
Rm - Tensile strength (MPa) (T5), (S)
140
Hardness
Brinell hardness (HB): (T5), (K)
50 - 60
Brinell hardness (HB): (T5), (S)
50 - 60
Registered Designations & Aliases
EN-MC65120EN-MCMgRE3Zn2Zr
Standards
EN 1753 EN 1753: 1997 Magnesium and magnesium alloys. Magnesium alloy ingots and castings