EN-MCMgZn4RE1Zr
Magnesium Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength210MPa
Yield Strength135MPa
Brinell Hardness55 - 70HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (T5), (K)
3
A - Min. elongation at fracture (%) (T5), (S)
2.5
R p0.2 0.2% proof strength (MPa) (T5), (K)
135
R p0.2 0.2% proof strength (MPa) (T5), (S)
135
Rm - Tensile strength (MPa) (T5), (K)
210
Rm - Tensile strength (MPa) (T5), (S)
200
Hardness
Brinell hardness (HB): (T5), (K)
55 - 70
Brinell hardness (HB): (T5), (S)
55 - 70
Registered Designations & Aliases
EN-MC35110EN-MCMgZn4RE1Zr
Standards
EN 1753 EN 1753: 1997 Magnesium and magnesium alloys. Magnesium alloy ingots and castings