EN-MCMgZn6Cu3Mn
Magnesium Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength195MPa
Yield Strength125MPa
Brinell Hardness55 - 65HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (T6), (K)
2
A - Min. elongation at fracture (%) (T6), (S)
2
R p0.2 0.2% proof strength (MPa) (T6), (K)
125
R p0.2 0.2% proof strength (MPa) (T6), (S)
125
Rm - Tensile strength (MPa) (T6), (K)
195
Rm - Tensile strength (MPa) (T6), (S)
195
Hardness
Brinell hardness (HB): (T6), (K)
55 - 65
Brinell hardness (HB): (T6), (S)
55 - 65
Registered Designations & Aliases
EN-MC32110EN-MCMgZn6Cu3Mn
Standards
EN 1753 EN 1753: 1997 Magnesium and magnesium alloys. Magnesium alloy ingots and castings