EN-MCMgAl9Zn1(A)
Magnesium Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength160MPa
Yield Strength90MPa
Brinell Hardness50 - 65HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (F), (S)
2
A - Min. elongation at fracture (%) (T4), (S)
6
A - Min. elongation at fracture (%) (T6), (S)
2
R p0.2 0.2% proof strength (MPa) (F), (S)
90
R p0.2 0.2% proof strength (MPa) (T4), (S)
110
R p0.2 0.2% proof strength (MPa) (T6), (S)
150
Rm - Tensile strength (MPa) (F), (S)
160
Rm - Tensile strength (MPa) (T4), (S)
240
Rm - Tensile strength (MPa) (T6), (S)
240
Hardness
Brinell hardness (HB): (F), (S)
50 - 65
Brinell hardness (HB): (T4), (S)
55 - 70
Brinell hardness (HB): (T6), (S)
60 - 90
Registered Designations & Aliases
EN-MC21120EN-MCMgAl9Zn1(A)
Standards
EN 1753 EN 1753: 1997 Magnesium and magnesium alloys. Magnesium alloy ingots and castings