CuZn35Mn2Al1Fe1-C
Copper Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength475MPa
Yield Strength200MPa
Brinell Hardness110HB
Maximum Service TemperatureUnknown
Chemical Composition
S
CuZn35Mn2Al1Fe1-C ( CC765S ) Copper-zinc alloy Chemical composition. Equivalents of CuZn35Mn2Al1Fe1-C ( CC765S ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation at fracture (%) (GM) or (GZ) or (GC)
18
A - Min. elongation at fracture (%) (GS)
20
R p0.2 0.2% proof strength (MPa) (GM)
200
R p0.2 0.2% proof strength (MPa) (GS)
170
R p0.2 0.2% proof strength (MPa) (GZ) or (GC)
200
Rm - Tensile strength (MPa) (GM)
475
Rm - Tensile strength (MPa) (GS)
450
Rm - Tensile strength (MPa) (GZ) or (GC)
500
Hardness
Brinell hardness (HBW): (GS) or (GM)
110
Brinell hardness (HBW): (GZ) or (GC)
120
Registered Designations & Aliases
CC765SCuZn35Mn2Al1Fe1-C
Standards
EN 1982 EN 1982: 2008 Copper and copper alloys. Ingots and castings