CuMn11Al8Fe3Ni3-C
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength630MPa
Yield Strength275MPa
Brinell Hardness150HB
Maximum Service TemperatureUnknown
Chemical Composition
C
CuMn11Al8Fe3Ni3-C ( CC212E ) Copper-manganese-aluminium alloy Chemical composition. Equivalents of CuMn11Al8Fe3Ni3-C ( CC212E ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation at fracture (%) (GS)
18
R p0.2 0.2% proof strength (MPa) (GS)
275
Rm - Tensile strength (MPa) (GS)
630
Hardness
Brinell hardness (HBW): (GS)
150
Other
GC
Continuous casting
GM
Permanent mould casting
GP
Pressure die casting
GS
Sand casting
GZ
Centrifugal casting
H
Material condition designated by the minimum value of hardness requirement for the product with mandatory hardness requirements
R
Material condition designated by the minimum value of tensile strength requirement for the product with mandatory tensile strength and elongation requirements
Registered Designations & Aliases
CC212ECuMn11Al8Fe3Ni3-C
Standards
EN 1982 EN 1982: 2008 Copper and copper alloys. Ingots and castings