CuAl11Fe6Ni6-C
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength750MPa
Yield Strength380MPa
Brinell Hardness185HB
Maximum Service TemperatureUnknown
Chemical Composition
C
CuAl11Fe6Ni6-C ( CC334G ) Copper-aluminium alloy Chemical composition. Equivalents of CuAl11Fe6Ni6-C ( CC334G ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation at fracture (%) (GS) or (GZ) or (GM)
5
R p0.2 0.2% proof strength (MPa) (GM) or (GZ)
380
R p0.2 0.2% proof strength (MPa) (GS)
320
Rm - Tensile strength (MPa) (GM) or (GZ)
750
Rm - Tensile strength (MPa) (GS)
680
Hardness
Brinell hardness (HBW): (GM) or (GZ)
185
Brinell hardness (HBW): (GS)
170
Registered Designations & Aliases
CC334GCuAl11Fe6Ni6-C
Standards
EN 1982 EN 1982: 2008 Copper and copper alloys. Ingots and castings