CuAl10Ni3Fe2-C
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength600MPa
Yield Strength250MPa
Brinell Hardness130HB
Maximum Service TemperatureUnknown
Chemical Composition
C
CuAl10Ni3Fe2-C ( CC332G ) Copper-aluminium alloy Chemical composition. Equivalents of CuAl10Ni3Fe2-C ( CC332G ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation at fracture (%) (GM) or (GZ) or (GC)
20
A - Min. elongation at fracture (%) (GS)
18
R p0.2 0.2% proof strength (MPa) (GM)
250
R p0.2 0.2% proof strength (MPa) (GS)
180
R p0.2 0.2% proof strength (MPa) (GZ) or (GC)
220
Rm - Tensile strength (MPa) (GM)
600
Rm - Tensile strength (MPa) (GS)
500
Rm - Tensile strength (MPa) (GZ) or (GC)
550
Hardness
Brinell hardness (HBW): (GM)
130
Brinell hardness (HBW): (GS)
100
Brinell hardness (HBW): (GZ) or (GC)
120
Registered Designations & Aliases
CC332GCuAl10Ni3Fe2-C
Standards
EN 1982 EN 1982: 2008 Copper and copper alloys. Ingots and castings