CuAl9-C
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength500MPa
Yield Strength180MPa
Brinell Hardness100HB
Maximum Service TemperatureUnknown
Chemical Composition
C
CuAl9-C ( CC330G ) Copper-aluminium alloy Chemical composition. Equivalents of CuAl9-C ( CC330G ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation at fracture (%) (GM)
20
A - Min. elongation at fracture (%) (GZ)
15
R p0.2 0.2% proof strength (MPa) (GM)
180
R p0.2 0.2% proof strength (MPa) (GZ)
160
Rm - Tensile strength (MPa) (GM)
500
Rm - Tensile strength (MPa) (GZ)
450
Hardness
Brinell hardness (HBW): (GM) or (GZ)
100
Other
H
Material condition designated by the minimum value of hardness requirement for the product with mandatory hardness requirements
R
Material condition designated by the minimum value of tensile strength requirement for the product with mandatory tensile strength and elongation requirements
Registered Designations & Aliases
CC330GCuAl9-C
Standards
EN 1982 EN 1982: 2008 Copper and copper alloys. Ingots and castings