UNS C12200 (CW024A) Phosphorized Copper

Copper Alloys

Material conditionO25 (hot rolled and annealed)

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density9g/cm³

Elastic Modulus120GPa

Tensile Strength230MPa

Yield Strength82MPa

Brinell HardnessUnknown

Maximum Service Temperature200°C

Weight Calculator

Chemical Composition

0.015 to 0.040%

99.9 to 99.985%

Mechanical

Elastic (Young's, Tensile) Modulus

120 GPa

Elongation at Break

45 %

Poisson's Ratio

0.34

Shear Modulus

43 GPa

Shear Strength

160 MPa

Tensile Strength: Ultimate (UTS)

230 MPa

Tensile Strength: Yield (Proof)

82 MPa

Hardness

Rockwell F Hardness

Rockwell Superficial 30T Hardness

Physical

Density

9.0 g/cm 3

Thermal

Latent Heat of Fusion

210 J/g

Maximum Temperature: Mechanical

200 °C

Melting Completion (Liquidus)

1080 °C

Melting Onset (Solidus)

1030 °C

Specific Heat Capacity

390 J/kg-K

Thermal Conductivity

340 W/m-K

Thermal Diffusivity

98 mm 2 /s

Thermal Expansion

17 µm/m-K

Thermal Shock Resistance

8.3 points

Electrical

Electrical Conductivity: Equal Volume

85 % IACS

Electrical Conductivity: Equal Weight (Specific)

85 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

82 MJ/m 3

Resilience: Unit (Modulus of Resilience)

29 kJ/m 3

Stiffness to Weight: Axial

7.2 points

Stiffness to Weight: Bending

18 points

Strength to Weight: Axial

7.2 points

Strength to Weight: Bending

9.4 points

Environmental

Base Metal Price

31 % relative

Embodied Carbon

2.6 kg CO 2 /kg material

Embodied Energy

41 MJ/kg

Embodied Energy

41 MJ/kg 18 x 10 3 BTU/lb

Embodied Water

310 L/kg

Embodied Water

310 L/kg 37 gal/lb

Registered Designations & Aliases

C12200CW024ACW024ACu-DHPUNS C12200 (CW024A) Phosphorized Copper

Standards

ASTM B111 ASTM B111: Standard Specification for Copper and Copper-Alloy Seamless Condenser Tubes and Ferrule Stock

ASTM B111 ASTM B111: Standard Specification for Copper and Copper-Alloy Seamless Condenser Tubes and Ferrule Stock ASTM B152: Standard Specification for Copper Sheet, Strip, Plate, and Rolled Bar Copper Alloys: Preparation, Properties and Applications, Michael Naboka and Jennifer Giordano (editors), 2013 Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993

ASTM B152 ASTM B152: Standard Specification for Copper Sheet, Strip, Plate, and Rolled Bar

EN 1172 EN 1172: 1997 Copper and copper alloys. Sheet and strip for building purposes

EN 12163 EN 12163: 1998 Copper and copper alloys. Rod for general purposes

EN 12165 EN 12165: 1998 Copper and copper alloys. Wrought and unwrought forging stock

EN 12166 EN 12166: 1998 Copper and copper alloys. Wire for general purposes

EN 12167 EN 12167: 1998 Copper and copper alloys. Profiles and rectangular bar for general purposes

EN 12420 EN 12420: 1999 Copper and copper alloys. Forgings

EN 12449 EN 12449: 1999 Copper and copper alloys. Seamless, round tubes for general purposes

EN 12451 EN 12451: 1999 Copper and copper alloys. Seamless, round tubes for heat exchangers

EN 12452 EN 12452: 1999 Copper and copper alloys. Rolled, finned, seamless tubes for heat exchangers

EN 13148 EN 13148: 2001 Copper and copper alloys. Hot-dip tinned strip

EN 1652 EN 1652: 1998 Copper and copper alloys. Plate, sheet, strip and circles for general purposes

EN 1653 EN 1653: 1998 Copper and copper alloys. Plate, sheet and circles for boilers, pressure vessels and hot water storage units

EN 1976 EN 1976: 1998 Copper and copper alloys. Cast unwrought copper products