CuSn8PbP
Copper Alloys
Property Overview
Density8.8g/cm³
Elastic ModulusUnknown
Tensile Strength460MPa
Yield Strength280MPa
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (R460)
30
A - Min. elongation at fracture (%) (R550)
12
A - Min. elongation at fracture (%) (R620)
5
R p0.2 0.2% proof strength (MPa) (R460)
280
R p0.2 0.2% proof strength (MPa) (R550)
480
R p0.2 0.2% proof strength (MPa) (R620)
540
Rm - Tensile strength (MPa) (R460)
460
Rm - Tensile strength (MPa) (R550)
550
Rm - Tensile strength (MPa) (R620)
620
Hardness
Vickers hardness ( HV): (H130) (R460)
130 - 165
Vickers hardness ( HV): (H165) (R550)
165 - 195
Vickers hardness ( HV): (H180) (R620)
180
Other
H
Material condition designated by the minimum value of hardness requirement for the product with mandatory hardness requirements
R
Material condition designated by the minimum value of tensile strength requirement for the product with mandatory tensile strength and elongation requirements
Registered Designations & Aliases
CW460KCuSn8PbP
Standards
EN 12449 EN 12449: 1999 Copper and copper alloys. Seamless, round tubes for general purposes