UNS C11100 Electrolytic Tough Pitch Copper
Copper Alloys
Property Overview
Density9g/cm³
Elastic Modulus120GPa
Tensile Strength460MPa
Yield Strength420MPa
Brinell HardnessUnknown
Maximum Service Temperature200°C
Chemical Composition
CU
99.9 to 100%
RES.
Residuals res. | | 0 to 0.1%
RESIDUALS RES.
0 to 0.1%
Mechanical
Elastic (Young's, Tensile) Modulus
120 GPa
Elongation at Break
1.5 %
Poisson's Ratio
0.34
Shear Modulus
44 GPa
Shear Strength
230 MPa
Tensile Strength: Ultimate (UTS)
460 MPa
Tensile Strength: Yield (Proof)
420 MPa
Physical
Density
9.0 g/cm 3
Thermal
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C
Melting Completion (Liquidus)
1080 °C
Melting Onset (Solidus)
1070 °C
Specific Heat Capacity
390 J/kg-K
Thermal Conductivity
390 W/m-K
Thermal Diffusivity
110 mm 2 /s
Thermal Expansion
17 µm/m-K
Thermal Shock Resistance
16 points
Electrical
Electrical Conductivity: Equal Volume
100 % IACS
Electrical Conductivity: Equal Weight (Specific)
100 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
6.6 MJ/m 3
Resilience: Unit (Modulus of Resilience)
750 kJ/m 3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
14 points
Strength to Weight: Bending
15 points
Environmental
Base Metal Price
31 % relative
Embodied Carbon
2.6 kg CO 2 /kg material
Embodied Energy
41 MJ/kg
Embodied Energy
41 MJ/kg 18 x 10 3 BTU/lb
Embodied Water
310 L/kg
Embodied Water
310 L/kg 37 gal/lb
Registered Designations & Aliases
C11100UNS C11100 Electrolytic Tough Pitch Copper