CuZn36Pb2As
Copper Alloys
Property Overview
Density8.4g/cm³
Elastic ModulusUnknown
Tensile Strength280MPa
Yield Strength120MPa
Brinell Hardness80HB
Maximum Service TemperatureUnknown
Chemical Composition
N
CuZn36Pb2As ( CW602N ) Copper-zinc-lead alloy Chemical composition. Equivalents of CuZn36Pb2As ( CW602N ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation at fracture (%) (R280)
30
A - Min. elongation at fracture (%) (R350)
25
R p0.2 0.2% proof strength (MPa) (R280)
120
R p0.2 0.2% proof strength (MPa) (R350)
150
Rm - Tensile strength (MPa) (R280)
280
Rm - Tensile strength (MPa) (R350)
350
Hardness
Brinell hardness (HB): (R280)
80
Brinell hardness (HB): (R350)
90
Other
H
Material condition designated by the minimum value of hardness requirement for the product with mandatory hardness requirements
R
Material condition designated by the minimum value of tensile strength requirement for the product with mandatory tensile strength and elongation requirements
Registered Designations & Aliases
CW602NCuZn36Pb2As
Standards
EN 12164 EN 12164: 1998 Copper and copper alloys. Rod for free machining purposes
EN 12165 EN 12165: 1998 Copper and copper alloys. Wrought and unwrought forging stock
EN 12167 EN 12167: 1998 Copper and copper alloys. Profiles and rectangular bar for general purposes
EN 12168 EN 12168: 1998 Copper and copper alloys. Hollow rod for free machining purposes
EN 12420 EN 12420: 1999 Copper and copper alloys. Forgings
EN 12449 EN 12449: 1999 Copper and copper alloys. Seamless, round tubes for general purposes