CuAl10Fe3Mn2
Wrought Aluminum Alloys
Property Overview
Density7.6g/cm³
Elastic ModulusUnknown
Tensile Strength590MPa
Yield Strength330MPa
Brinell Hardness170HB
Maximum Service TemperatureUnknown
Chemical Composition
MN
CuAl10Fe3Mn2 ( CW306G ) Copper-aluminium alloy Chemical composition. Equivalents of CuAl10Fe3Mn2 ( CW306G ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation at fracture (%) (R590)
12
A - Min. elongation at fracture (%) (R690)
6
R p0.2 0.2% proof strength (MPa) (R590)
330
R p0.2 0.2% proof strength (MPa) (R690)
510
Rm - Tensile strength (MPa) (R590)
590
Rm - Tensile strength (MPa) (R690)
690
Hardness
Brinell hardness (HB): (H140)(R590)
140 - 180
Brinell hardness (HB): (H170)(R690)
170
Registered Designations & Aliases
CW306GCuAl10Fe3Mn2
Standards
EN 12163 EN 12163: 1998 Copper and copper alloys. Rod for general purposes
EN 12165 EN 12165: 1998 Copper and copper alloys. Wrought and unwrought forging stock
EN 12167 EN 12167: 1998 Copper and copper alloys. Profiles and rectangular bar for general purposes
EN 12420 EN 12420: 1999 Copper and copper alloys. Forgings