ENAC-AlSi10MnMg
Cast Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength250MPa
Yield Strength120MPa
Brinell Hardness65HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (F) (D)
5
A - Min. elongation at fracture (%) (T5) (D)
4
A - Min. elongation at fracture (%) (T7) (D)
12
R p0.2 0.2% proof strength (MPa) (F) (D)
120
R p0.2 0.2% proof strength (MPa) (T5) (D)
150
R p0.2 0.2% proof strength (MPa) (T7) (D)
120
Rm - Tensile strength (MPa) (F) (D)
250
Rm - Tensile strength (MPa) (T5) (D)
270
Rm - Tensile strength (MPa) (T7) (D)
200
Hardness
Brinell hardness (HBW): (F) (D)
65
Brinell hardness (HBW): (T5) (D)
80
Brinell hardness (HBW): (T7) (D)
60
Registered Designations & Aliases
ENAC-43500ENAC-AlSi10MnMg
Standards
EN 1706 EN 1706: 2010 Aluminium and aluminium alloys. Castings. Chemical composition and mechanical properties