ENAC-AlCu4MgTi
Cast Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength320MPa
Yield Strength200MPa
Brinell Hardness90HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (T4) (K)
8
A - Min. elongation at fracture (%) (T4) (L)
5
A - Min. elongation at fracture (%) (T4) (S)
5
R p0.2 0.2% proof strength (MPa) (T4) (K)
200
R p0.2 0.2% proof strength (MPa) (T4) (L)
220
R p0.2 0.2% proof strength (MPa) (T4) (S)
200
Rm - Tensile strength (MPa) (T4) (K)
320
Rm - Tensile strength (MPa) (T4) (L)
300
Rm - Tensile strength (MPa) (T4) (S)
300
Hardness
Brinell hardness (HBW): (T4) (K)
90
Brinell hardness (HBW): (T4) (L)
90
Brinell hardness (HBW): (T4) (S)
90
Registered Designations & Aliases
ENAC-21000ENAC-AlCu4MgTi
Standards
EN 1706 EN 1706: 2010 Aluminium and aluminium alloys. Castings. Chemical composition and mechanical properties