UNS C77100 Nickel Silver
Nickel Alloys
Property Overview
Density8.1g/cm³
Elastic Modulus110GPa
Tensile Strength600MPa
Yield Strength540MPa
Brinell HardnessUnknown
Maximum Service Temperature150°C
Chemical Composition
NI
9.0 to 12%
MN
0 to 0.9%
CU
52 to 56%
PB
0 to 0.030%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
ZN
30.6 to 39%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Poisson's Ratio
0.31
Shear Modulus
45 GPa
Tensile Strength: Ultimate (UTS)
600 MPa
Tensile Strength: Yield (Proof)
540 MPa
Physical
Density
8.1 g/cm 3
Thermal
Latent Heat of Fusion
180 J/g
Maximum Temperature: Mechanical
150 °C
Melting Completion (Liquidus)
990 °C
Melting Onset (Solidus)
950 °C
Specific Heat Capacity
390 J/kg-K
Thermal Conductivity
40 W/m-K
Thermal Diffusivity
13 mm 2 /s
Thermal Expansion
20 µm/m-K
Thermal Shock Resistance
19 points
Electrical
Electrical Conductivity: Equal Volume
7.6 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.5 % IACS
Calculated
Resilience: Unit (Modulus of Resilience)
1280 kJ/m 3
Stiffness to Weight: Axial
7.8 points
Stiffness to Weight: Bending
20 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
20 points
Environmental
Base Metal Price
27 % relative
Embodied Carbon
3.5 kg CO 2 /kg material
Embodied Energy
56 MJ/kg
Embodied Energy
56 MJ/kg 24 x 10 3 BTU/lb
Embodied Water
310 L/kg
Embodied Water
310 L/kg 37 gal/lb
Registered Designations & Aliases
C77100UNS C77100 Nickel Silver