UNS C76400 Nickel Silver
Nickel Alloys
H01 (quarter hard)
Property Overview
Density8.4g/cm³
Elastic Modulus120GPa
Tensile Strength590MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service Temperature190°C
Chemical Composition
NI
16.5 to 19.5%
MN
0 to 0.5%
CU
58.5 to 61.5%
PB
0 to 0.050%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
ZN
17.7 to 25%
FE
0 to 0.25%
Mechanical
Elastic (Young's, Tensile) Modulus
120 GPa
Poisson's Ratio
0.32
Shear Modulus
46 GPa
Tensile Strength: Ultimate (UTS)
590 MPa
Physical
Density
8.4 g/cm 3
Thermal
Latent Heat of Fusion
200 J/g
Maximum Temperature: Mechanical
190 °C
Melting Completion (Liquidus)
990 °C
Melting Onset (Solidus)
950 °C
Specific Heat Capacity
400 J/kg-K
Thermal Conductivity
31 W/m-K
Thermal Diffusivity
9.3 mm 2 /s
Thermal Expansion
18 µm/m-K
Thermal Shock Resistance
19 points
Electrical
Electrical Conductivity: Equal Volume
5.7 % IACS
Electrical Conductivity: Equal Weight (Specific)
6.1 % IACS
Calculated
Stiffness to Weight: Axial
8.1 points
Stiffness to Weight: Bending
20 points
Strength to Weight: Axial
19 points
Strength to Weight: Bending
18 points
Environmental
Base Metal Price
32 % relative
Embodied Carbon
4.1 kg CO 2 /kg material
Embodied Energy
63 MJ/kg
Embodied Energy
63 MJ/kg 27 x 10 3 BTU/lb
Embodied Water
300 L/kg
Embodied Water
300 L/kg 36 gal/lb
Registered Designations & Aliases
C76400UNS C76400 Nickel Silver
Standards
ASTM B151 ASTM B151: Standard Specification for Copper-Nickel-Zinc Alloy (Nickel Silver) and Copper-Nickel Rod and Bar