ENAW-AlMg0.9Si0.9MnCu
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength320MPa
Yield Strength220MPa
Brinell Hardness85HB
Maximum Service TemperatureUnknown
Chemical Composition
SI
ENAW-AlMg0.9Si0.9MnCu ( ENAW-6110A ) Aluminium - 6000 series ( Magnesium Mg and Silicon Si are major alloying elements ) Chemical composition. Equivalents of ENAW-AlMg0.9Si0.9MnCu ( ENAW-6110A ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation Lo = 50mm (%) (T4)
14
A - Min. elongation Lo = 50mm (%) (T5)
8
A - Min. elongation Lo = 50mm (%) (T6)
8
A - Min. elongation at fracture (%) (T4)
16
A - Min. elongation at fracture (%) (T5)
10
A - Min. elongation at fracture (%) (T6)
10
R p0.2 0.2% proof strength (MPa) (T4)
220
R p0.2 0.2% proof strength (MPa) (T5)
360
R p0.2 0.2% proof strength (MPa) (T6)
360-380
Rm - Tensile strength (MPa) (T4)
320
Rm - Tensile strength (MPa) (T5)
380
Rm - Tensile strength (MPa) (T6)
380-410
Hardness
Brinell hardness (HBW): (T4)
85
Brinell hardness (HBW): (T5)
115
Brinell hardness (HBW): (T6)
120
Other
F
Fabricated (as cast)
H
Strain hardened
O
Annealed
T
Thermally treated to produce stable tempers other than F, O or H
T1
Cooled from an elevated temperature shaping process and naturally aged
T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
T3
Solution heat treated, cold worked and naturally aged
T4
Solution heat treated and naturally aged
T5
Cooled from an elevated temperature shaping process and then artificially aged
T6
Solution heat treated and then artificially aged
T7
Solution heat treated and then artificially overaged (stabilised)
T8
Solution heat treated, cold worked and then artificially aged
T9
Solution heat treated, artificially aged and then cold worked
W
Solution heat treated (unstable temper)
Registered Designations & Aliases
ENAW-6110AENAW-AlMg0.9Si0.9MnCu
Standards
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 755-2 EN 755-2: 2008 Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties