ENAW-AlMg0.7Si
Wrought Aluminum Alloys
Property Overview
Density2.7g/cm³
Elastic ModulusUnknown
Tensile Strength130MPa
Yield Strength65MPa
Brinell Hardness37HB
Maximum Service TemperatureUnknown
Chemical Composition
SI
ENAW-AlMg0.7Si ( ENAW-6063 ) Aluminium - 6000 series / Attention! Grade ENAW-6201 also named ENAW-AlMg0.7Si Chemical composition. Equivalents of ENAW-AlMg0.7Si ( ENAW-6063 ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation Lo = 50mm (%) (O) (H111)
16
A - Min. elongation Lo = 50mm (%) (T4)
10-12
A - Min. elongation Lo = 50mm (%) (T5)
5-6
A - Min. elongation Lo = 50mm (%) (T6)
6-8
A - Min. elongation at fracture (%) (O) (H111)
18
A - Min. elongation at fracture (%) (T4)
12-14
A - Min. elongation at fracture (%) (T5)
7-8
A - Min. elongation at fracture (%) (T6)
8-10
R p0.2 0.2% proof strength (MPa) (T4)
65
R p0.2 0.2% proof strength (MPa) (T5)
110-130
R p0.2 0.2% proof strength (MPa) (T6)
160-170
Rm - Tensile strength (MPa) (O) (H111)
130
Rm - Tensile strength (MPa) (T4)
120-130
Rm - Tensile strength (MPa) (T5)
160-175
Rm - Tensile strength (MPa) (T6)
195-215
Hardness
Brinell hardness (HBW): (O)
37
Brinell hardness (HBW): (O) (H111)
25
Brinell hardness (HBW): (T4)
50
Brinell hardness (HBW): (T5)
65
Brinell hardness (HBW): (T6)
75
Other
T
Thermally treated to produce stable tempers other than F, O or H
T1
Cooled from an elevated temperature shaping process and naturally aged
T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
T3
Solution heat treated, cold worked and naturally aged
T4
Solution heat treated and naturally aged
T5
Cooled from an elevated temperature shaping process and then artificially aged
T6
Solution heat treated and then artificially aged
T7
Solution heat treated and then artificially overaged (stabilised)
T8
Solution heat treated, cold worked and then artificially aged
T9
Solution heat treated, artificially aged and then cold worked
W
Solution heat treated (unstable temper)
Registered Designations & Aliases
ENAW-6063ENAW-AlMg0.7Si
Standards
EN 1301-2 EN 1301-2: 1997 Aluminium and aluminium alloys. Drawn wire. Mechanical properties
EN 1715-3 EN 1715-3: 2008 Aluminium and aluminium alloys. Drawing stock. Specific requirements for mechanical uses (excluding welding)
EN 570 EN 570: 2007 Aluminium and aluminium alloys. Impact extrusion slugs obtained from wrought products. Specification
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 683-2 EN 683-2: 2006 Aluminium and aluminium alloys. Finstock. Mechanical properties
EN 754-2 EN 754-2: 2008 Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties
EN 755-2 EN 755-2: 2008 Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties