ENAW-AlSi1MgCuMn
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength160-230MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
SI
ENAW-AlSi1MgCuMn ( ENAW-6056 ) Aluminium - 6000 series ( Magnesium Mg and Silicon Si are major alloying elements ) Chemical composition. Equivalents of ENAW-AlSi1MgCuMn ( ENAW-6056 ). Standards.1 Mechanical Properties. Hardness%
Mechanical
Rm - Tensile strength (MPa) (F)
160-230
Rm - Tensile strength (MPa) (O3)
140-180
Rm - Tensile strength (MPa) (T4)
300-380
Other
F
Fabricated (as cast)
H
Strain hardened
O
Annealed
T
Thermally treated to produce stable tempers other than F, O or H
T1
Cooled from an elevated temperature shaping process and naturally aged
T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
T3
Solution heat treated, cold worked and naturally aged
T4
Solution heat treated and naturally aged
T5
Cooled from an elevated temperature shaping process and then artificially aged
T6
Solution heat treated and then artificially aged
T7
Solution heat treated and then artificially overaged (stabilised)
T8
Solution heat treated, cold worked and then artificially aged
T9
Solution heat treated, artificially aged and then cold worked
W
Solution heat treated (unstable temper)
Registered Designations & Aliases
ENAW-6056ENAW-AlSi1MgCuMn
Standards
EN 1715-3 EN 1715-3: 2008 Aluminium and aluminium alloys. Drawing stock. Specific requirements for mechanical uses (excluding welding)
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products