ENAW-AlMg0.9Si0.9Cu
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength340MPa
Yield Strength320MPa
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
CU
ENAW-AlMg0.9Si0.9Cu ( ENAW-6011 ) Aluminium - 6000 series ( Magnesium Mg and Silicon Si are major alloying elements ) Chemical composition. Equivalents of ENAW-AlMg0.9Si0.9Cu ( ENAW-6011 ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation Lo = 50mm (%) (T8)
2
R p0.2 0.2% proof strength (MPa) (T8)
320
Rm - Tensile strength (MPa) (T8)
340
Other
F
Fabricated (as cast)
H
Strain hardened
O
Annealed
T
Thermally treated to produce stable tempers other than F, O or H
T1
Cooled from an elevated temperature shaping process and naturally aged
T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
T3
Solution heat treated, cold worked and naturally aged
T4
Solution heat treated and naturally aged
T5
Cooled from an elevated temperature shaping process and then artificially aged
T6
Solution heat treated and then artificially aged
T7
Solution heat treated and then artificially overaged (stabilised)
T8
Solution heat treated, cold worked and then artificially aged
T9
Solution heat treated, artificially aged and then cold worked
W
Solution heat treated (unstable temper)
Registered Designations & Aliases
ENAW-6011ENAW-AlMg0.9Si0.9Cu
Standards
EN 1396 EN 1396: 2007 Aluminium and aluminium alloys. Coil coated sheet and strip for general applications. Specifications
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products