ENAW-AlMg4.5Mn0.9
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength340-400MPa
Yield Strength270MPa
Brinell Hardness105HB
Maximum Service TemperatureUnknown
Chemical Composition
MN
ENAW-AlMg4.5Mn0.9 ( ENAW-5383 ) Aluminium - 5000 series ( Magnesium Mg is major alloying element ) Chemical composition. Equivalents of ENAW-AlMg4.5Mn0.9 ( ENAW-5383 ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation Lo = 50mm (%) (H24)
4-8
A - Min. elongation Lo = 50mm (%) (O)
11-16
R p0.2 0.2% proof strength (MPa) (H24)
270
R p0.2 0.2% proof strength (MPa) (O)
125-145
Rm - Tensile strength (MPa) (H24)
340-400
Rm - Tensile strength (MPa) (O)
270-360
Hardness
Brinell hardness (HBW): (H24)
105
Brinell hardness (HBW): (O)
75 - 85
Other
F
Fabricated (as cast)
H
Strain hardened
O
Annealed
T
Thermally treated to produce stable tempers other than F, O or H
T1
Cooled from an elevated temperature shaping process and naturally aged
T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
T3
Solution heat treated, cold worked and naturally aged
T4
Solution heat treated and naturally aged
T5
Cooled from an elevated temperature shaping process and then artificially aged
T6
Solution heat treated and then artificially aged
T7
Solution heat treated and then artificially overaged (stabilised)
T8
Solution heat treated, cold worked and then artificially aged
T9
Solution heat treated, artificially aged and then cold worked
W
Solution heat treated (unstable temper)
Registered Designations & Aliases
ENAW-5383ENAW-AlMg4.5Mn0.9
Standards
EN 485-2 EN 485-2: 2008 Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products