ENAW-AlMg0.5Mn
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength175MPa
Yield Strength115MPa
Brinell Hardness45HB
Maximum Service TemperatureUnknown
Chemical Composition
MN
ENAW-AlMg0.5Mn ( ENAW-5010 ) Aluminium - 5000 series ( Magnesium Mg is major alloying element ) Chemical composition. Equivalents of ENAW-AlMg0.5Mn ( ENAW-5010 ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation Lo = 50mm (%) (H14)
2-4
A - Min. elongation Lo = 50mm (%) (H18)
1-2
A - Min. elongation Lo = 50mm (%) (O)
17-24
R p0.2 0.2% proof strength (MPa) (H14)
115
R p0.2 0.2% proof strength (MPa) (H18)
160
R p0.2 0.2% proof strength (MPa) (O)
35
Rm - Tensile strength (MPa) (H14)
140-175
Rm - Tensile strength (MPa) (H18)
175
Rm - Tensile strength (MPa) (O)
90-130
Hardness
Brinell hardness (HBW): (H14)
45
Brinell hardness (HBW): (H18)
58
Brinell hardness (HBW): (O)
27
Other
F
Fabricated (as cast)
H
Strain hardened
O
Annealed
T
Thermally treated to produce stable tempers other than F, O or H
T1
Cooled from an elevated temperature shaping process and naturally aged
T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
T3
Solution heat treated, cold worked and naturally aged
T4
Solution heat treated and naturally aged
T5
Cooled from an elevated temperature shaping process and then artificially aged
T6
Solution heat treated and then artificially aged
T7
Solution heat treated and then artificially overaged (stabilised)
T8
Solution heat treated, cold worked and then artificially aged
T9
Solution heat treated, artificially aged and then cold worked
W
Solution heat treated (unstable temper)
Registered Designations & Aliases
ENAW-5010ENAW-AlMg0.5Mn
Standards
EN 1396 EN 1396: 2007 Aluminium and aluminium alloys. Coil coated sheet and strip for general applications. Specifications
EN 485-2 EN 485-2: 2008 Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products