ENAW-AlMg1(C)
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength100MPa
Yield Strength40MPa
Brinell Hardness30HB
Maximum Service TemperatureUnknown
Chemical Composition
C
ENAW-AlMg1(C) ( ENAW-5005A ) Aluminium - 5000 series ( Magnesium Mg is major alloying element ) Chemical composition. Equivalents of ENAW-AlMg1(C) ( ENAW-5005A ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation Lo = 50mm (%) (F) (H112)
16
A - Min. elongation Lo = 50mm (%) (H18)
1-2
A - Min. elongation Lo = 50mm (%) (O) (H111)
16-18
A - Min. elongation at fracture (%) (F) (H112)
18
A - Min. elongation at fracture (%) (O) (H111)
18-20
R p0.2 0.2% proof strength (MPa) (F) (H112)
40
R p0.2 0.2% proof strength (MPa) (H18)
165
R p0.2 0.2% proof strength (MPa) (O) (H111)
40
Rm - Tensile strength (MPa) (F) (H112)
100
Rm - Tensile strength (MPa) (H18)
185
Rm - Tensile strength (MPa) (O) (H111)
100-150
Hardness
Brinell hardness (HBW): (F) (H112)
30
Brinell hardness (HBW): (H18)
58
Brinell hardness (HBW): (O) (H111)
30
Registered Designations & Aliases
ENAW-5005AENAW-AlMg1(C)
Standards
EN 12392 EN 12392: 2000 Aluminium and aluminium alloys. Wrought products. Special requirements for products intended for the production of pressure equipment
EN 485-2 EN 485-2: 2008 Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
EN 570 EN 570: 2007 Aluminium and aluminium alloys. Impact extrusion slugs obtained from wrought products. Specification
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 754-2 EN 754-2: 2008 Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties
EN 755-2 EN 755-2: 2008 Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties