ENAW-AlMn0.2
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength80MPa
Yield Strength30MPa
Brinell Hardness23HB
Maximum Service TemperatureUnknown
Chemical Composition
MN
ENAW-AlMn0.2 ( ENAW-3102 ) Aluminium - 3000 series ( Manganese Mn is major alloying element) Chemical composition. Equivalents of ENAW-AlMn0.2 ( ENAW-3102 ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation Lo = 50mm (%) (F) (H112)
23
A - Min. elongation at fracture (%) (F) (H112)
25
R p0.2 0.2% proof strength (MPa) (F) (H112)
30
Rm - Tensile strength (MPa) (F) (H112)
80
Hardness
Brinell hardness (HBW): (F) (H112)
23
Brinell hardness (HBW): (O)
23
Other
F
Fabricated (as cast)
H
Strain hardened
O
Annealed
T
Thermally treated to produce stable tempers other than F, O or H
T1
Cooled from an elevated temperature shaping process and naturally aged
T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
T3
Solution heat treated, cold worked and naturally aged
T4
Solution heat treated and naturally aged
T5
Cooled from an elevated temperature shaping process and then artificially aged
T6
Solution heat treated and then artificially aged
T7
Solution heat treated and then artificially overaged (stabilised)
T8
Solution heat treated, cold worked and then artificially aged
T9
Solution heat treated, artificially aged and then cold worked
W
Solution heat treated (unstable temper)
Registered Designations & Aliases
ENAW-3102ENAW-AlMn0.2
Standards
EN 570 EN 570: 2007 Aluminium and aluminium alloys. Impact extrusion slugs obtained from wrought products. Specification
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 755-2 EN 755-2: 2008 Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties