UNS C72500 (CW351H) Tin-Bearing Copper-Nickel

Other

Material conditionH01 (quarter hard)

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.9g/cm³

Elastic Modulus120GPa

Tensile Strength450MPa

Yield StrengthUnknown

Brinell HardnessUnknown

Maximum Service Temperature210°C

Weight Calculator

Chemical Composition

8.5 to 10.5%

0 to 0.2%

85.2 to 89.7%

0 to 0.050%

RES.

Residuals res. | | 0 to 0.2%

RESIDUALS RES.

0 to 0.2%

1.8 to 2.8%

0 to 0.5%

0 to 0.6%

Mechanical

Elastic (Young's, Tensile) Modulus

120 GPa

Poisson's Ratio

0.34

Shear Modulus

45 GPa

Tensile Strength: Ultimate (UTS)

450 MPa

Hardness

Rockwell B Hardness

Rockwell Superficial 30T Hardness

Rockwell Superficial 30T Hardness 62

Rockwell Superficial 30T Hardness

Physical

Density

8.9 g/cm 3

Thermal

Latent Heat of Fusion

210 J/g

Maximum Temperature: Mechanical

210 °C

Melting Completion (Liquidus)

1130 °C

Melting Onset (Solidus)

1060 °C

Specific Heat Capacity

390 J/kg-K

Thermal Conductivity

54 W/m-K

Thermal Diffusivity

16 mm 2 /s

Thermal Expansion

17 µm/m-K

Thermal Shock Resistance

16 points

Electrical

Electrical Conductivity: Equal Volume

11 % IACS

Electrical Conductivity: Equal Weight (Specific)

11 % IACS

Calculated

Stiffness to Weight: Axial

7.6 points

Stiffness to Weight: Bending

19 points

Strength to Weight: Axial

14 points

Strength to Weight: Bending

15 points

Environmental

Base Metal Price

35 % relative

Embodied Carbon

3.6 kg CO 2 /kg material

Embodied Energy

55 MJ/kg

Embodied Energy

55 MJ/kg 24 x 10 3 BTU/lb

Embodied Water

320 L/kg

Embodied Water

320 L/kg 38 gal/lb

Registered Designations & Aliases

C72500CW351HCW351HCuNi9Sn2UNS C72500 (CW351H) Tin-Bearing Copper-Nickel

Standards

ASTM B122 ASTM B122: Standard Specification for Copper-Nickel-Tin Alloy, Copper-Nickel-Zinc Alloy (Nickel Silver), and Copper-Nickel Alloy Plate, Sheet, Strip, and Rolled Bar

EN 13148 EN 13148: 2001 Copper and copper alloys. Hot-dip tinned strip

EN 1652 EN 1652: 1998 Copper and copper alloys. Plate, sheet, strip and circles for general purposes

EN 1654 EN 1654: 1998 Copper and copper alloys. Strip for springs and connectors