ENAW-AlCu6BiPb(A)
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength275MPa
Yield Strength125MPa
Brinell Hardness95HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 50mm (%) (T4)
12
A - Min. elongation Lo = 50mm (%) (T6)
4-6
A - Min. elongation at fracture (%) (T4)
14
A - Min. elongation at fracture (%) (T6)
6-8
R p0.2 0.2% proof strength (MPa) (T4)
125
R p0.2 0.2% proof strength (MPa) (T6)
195-230
Rm - Tensile strength (MPa) (T4)
275
Rm - Tensile strength (MPa) (T6)
295-310
Hardness
Brinell hardness (HBW): (T4)
95
Brinell hardness (HBW): (T6)
110
Other
F
Fabricated (as cast)
H
Strain hardened
O
Annealed
T
Thermally treated to produce stable tempers other than F, O or H
T1
Cooled from an elevated temperature shaping process and naturally aged
T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
T3
Solution heat treated, cold worked and naturally aged
T4
Solution heat treated and naturally aged
T5
Cooled from an elevated temperature shaping process and then artificially aged
T6
Solution heat treated and then artificially aged
T7
Solution heat treated and then artificially overaged (stabilised)
T8
Solution heat treated, cold worked and then artificially aged
T9
Solution heat treated, artificially aged and then cold worked
W
Solution heat treated (unstable temper)
Registered Designations & Aliases
ENAW-2011AENAW-AlCu6BiPb(A)
Standards
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 754-2 EN 754-2: 2008 Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties
EN 755-2 EN 755-2: 2008 Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties