ENAW-AlCu6BiPb
Wrought Aluminum Alloys
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength275MPa
Yield Strength125MPa
Brinell Hardness50HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 50mm (%) (T4)
12
A - Min. elongation Lo = 50mm (%) (T6)
4-6
A - Min. elongation at fracture (%) (T4)
14
A - Min. elongation at fracture (%) (T6)
6-8
R p0.2 0.2% proof strength (MPa) (T4)
125
R p0.2 0.2% proof strength (MPa) (T6)
195-230
Rm - Tensile strength (MPa) (T4)
275
Rm - Tensile strength (MPa) (T6)
295-310
Hardness
Brinell hardness (HBW): (O)
50
Brinell hardness (HBW): (T4)
95
Brinell hardness (HBW): (T6)
110
Registered Designations & Aliases
ENAW-2011ENAW-AlCu6BiPb
Standards
EN 1301-2 EN 1301-2: 1997 Aluminium and aluminium alloys. Drawn wire. Mechanical properties
EN 1715-3 EN 1715-3: 2008 Aluminium and aluminium alloys. Drawing stock. Specific requirements for mechanical uses (excluding welding)
EN 570 EN 570: 2007 Aluminium and aluminium alloys. Impact extrusion slugs obtained from wrought products. Specification
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 754-2 EN 754-2: 2008 Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties
EN 755-2 EN 755-2: 2008 Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties