ENAW-Al99.0Cu
Wrought Aluminum Alloys
Property Overview
Density2.71g/cm³
Elastic ModulusUnknown
Tensile Strength180MPa
Yield Strength100MPa
Brinell Hardness28HB
Maximum Service TemperatureUnknown
Chemical Composition
CU
ENAW-Al99.0Cu ( ENAW-1100 ) Aluminium - 1000 series ( Al 99.00% and greater ) Chemical composition. Equivalents of ENAW-Al99.0Cu ( ENAW-1100 ). Standards.1 Mechanical Properties. Hardness%
Mechanical
A - Min. elongation Lo = 50mm (%) (H14)
1
A - Min. elongation Lo = 50mm (%) (H19)
1
R p0.2 0.2% proof strength (MPa) (H14)
100
R p0.2 0.2% proof strength (MPa) (H19)
160
Rm - Tensile strength (MPa) (H14)
110-160
Rm - Tensile strength (MPa) (H19)
180
Hardness
Brinell hardness (HBW): (O)
28
Other
F
Fabricated (as cast)
H
Strain hardened
O
Annealed
T
Thermally treated to produce stable tempers other than F, O or H
T1
Cooled from an elevated temperature shaping process and naturally aged
T2
Cooled from an elevated temperature shaping process, cold worked and naturally aged
T3
Solution heat treated, cold worked and naturally aged
T4
Solution heat treated and naturally aged
T5
Cooled from an elevated temperature shaping process and then artificially aged
T6
Solution heat treated and then artificially aged
T7
Solution heat treated and then artificially overaged (stabilised)
T8
Solution heat treated, cold worked and then artificially aged
T9
Solution heat treated, artificially aged and then cold worked
W
Solution heat treated (unstable temper)
Registered Designations & Aliases
ENAW-1100ENAW-Al99.0Cu
Standards
EN 570 EN 570: 2007 Aluminium and aluminium alloys. Impact extrusion slugs obtained from wrought products. Specification
EN 573-3 EN 573-3: 2009 Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
EN 683-2 EN 683-2: 2006 Aluminium and aluminium alloys. Finstock. Mechanical properties