S960Q
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength980-1150MPa
Yield Strength960MPa
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 5,65 √ So (%)
10
KV - Impact energy (J) longitud.,
0° 40
KV - Impact energy (J) longitud.,
-20° 30
ReH - Minimum yield strength (MPa)
960
Rm - Tensile strength (MPa)
980-1150
Hardness
+A Soft annealed +AC Annealed to achieve spheroidization of the carbides +AR As rolled +AT Solution annealed +C Cold drawn / hard +CR Cold rolled +FP Treated to ferrite-pearlite structure and hardness range +I Isothermal annealing +LC Cold drawn / soft +M Thermo mechanical rolling +N Normalized +NT Normalized and tempered
+P Precipitation hardened +PE Peeled +QA Air quenched and tempered +QL Liquid quenched and tempered +QT Quenched and tempered +S Treated to improve shearability +SH As rolled and turned +SR Cold drawn and stress relieved +T Tempered +TH Treated to hardness range +WW Warm worked +U Untreated
Other
Nominal thickness (mm):
3 - 50
Registered Designations & Aliases
1.8941S960Q
Standards
EN 10025-6 EN 10025-6: 2004 Hot rolled products of structural steels. Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition
EN 10137-2 EN 10137-2: 1996 Plates and wide flats made of high yield strength structural steels in the quenched and tempered or precipitation hardened conditions. Delivery conditions for quenched and tempered steels