S275MH
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength360-510MPa
Yield Strength275MPa
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%)
24
KV - Impact energy (J)
-20° 40
ReH - Minimum yield strength (MPa)
275
ReH - Minimum yield strength (MPa)
265
Rm - Tensile strength (MPa)
360-510
Hardness
+A Soft annealed +AC Annealed to achieve spheroidization of the carbides +AR As rolled +AT Solution annealed +C Cold drawn / hard +CR Cold rolled +FP Treated to ferrite-pearlite structure and hardness range +I Isothermal annealing +LC Cold drawn / soft +M Thermo mechanical rolling +N Normalized +NT Normalized and tempered
+P Precipitation hardened +PE Peeled +QA Air quenched and tempered +QL Liquid quenched and tempered +QT Quenched and tempered +S Treated to improve shearability +SH As rolled and turned +SR Cold drawn and stress relieved +T Tempered +TH Treated to hardness range +WW Warm worked +U Untreated
Other
Nominal thickness (mm):
to 40
Nominal thickness (mm):
to 16
Nominal thickness (mm):
16 - 40
Registered Designations & Aliases
1.8843S275MH
Standards
EN 10219-1 EN 10219-1: 2006 Cold formed welded structural hollow sections of non-alloy and fine grain steels. Technical delivery requirements