30NiCrMo16-6
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength1080-1230MPa
Yield Strength880MPa
Brinell Hardness270HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 5,65 √ So (%) (+QT), round products
10
A - Min. elongation Lo = 5,65 √ So (%) (+QT), round products
11
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+QT)
880
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+QT)
790
Rm - Tensile strength (MPa) (+QT)
1080-1230
Rm - Tensile strength (MPa) (+QT)
900-1050
Hardness
Brinell hardness (HBW): (+A)
270
Other
Nominal diameter (mm):
to 16
Nominal diameter (mm):
16 - 40
Nominal diameter (mm):
40 - 100
Nominal diameter (mm):
100 - 160
Nominal diameter (mm):
160 - 250
Nominal diameter(mm): or for flat products thickness: to 8; 8-20; 20-60; 60-100; 100-160;
to 16
Nominal diameter(mm): or for flat products thickness: to 8; 8-20; 20-60; 60-100; 100-160;
16 - 40
Nominal diameter(mm): or for flat products thickness: to 8; 8-20; 20-60; 60-100; 100-160;
40 - 100
Nominal diameter(mm): or for flat products thickness: to 8; 8-20; 20-60; 60-100; 100-160;
100 - 160
Nominal diameter(mm): or for flat products thickness: to 8; 8-20; 20-60; 60-100; 100-160;
160 - 250
Nominal thickness (mm):
to 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 100
Nominal thickness (mm):
100 - 160
Nominal thickness (mm):
160 - 250
Registered Designations & Aliases
1.674730NiCrMo16-6
Standards
EN 10083-3 EN 10083-3: 2006 Steels for quenching and tempering. Technical delivery conditions for alloy steels