X40CrSiMo10-2
Other Steels
Property Overview
Density7.7g/cm³
Elastic ModulusUnknown
Tensile Strength900-1100MPa
Yield Strength700MPa
Brinell Hardness300HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (+QT)
14
R p0.2 0.2% proof strength (MPa) (+QT)
700
R p0.2 0.2% proof strength (MPa) (+QT)
700
+QT
Rm - Tensile strength (MPa) (+QT)
900-1100
Hardness
+A Soft annealed +AC Annealed to achieve spheroidization of the carbides +AR As rolled +AT Solution annealed +C Cold drawn / hard +CR Cold rolled +FP Treated to ferrite-pearlite structure and hardness range +I Isothermal annealing +LC Cold drawn / soft +M Thermo mechanical rolling +N Normalized +NT Normalized and tempered
+P Precipitation hardened +PE Peeled +QA Air quenched and tempered +QL Liquid quenched and tempered +QT Quenched and tempered +S Treated to improve shearability +SH As rolled and turned +SR Cold drawn and stress relieved +T Tempered +TH Treated to hardness range +WW Warm worked +U Untreated
Brinell hardness (HB): (+A)
300
Brinell hardness (HB): (+QT)
266 - 325
Other
Z - Reduction in cross section on fracture (%) (+QT)
40
Registered Designations & Aliases
1.4731X40CrSiMo10-2
Standards
EN 10090 EN 10090: 1998 Valve steels and alloys for internal combustion engines