38MnVS6
Carbon & Non-Alloy Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength800-950MPa
Yield Strength520MPa
Brinell Hardness255HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (+P)
12
R p0.2 0.2% proof strength (MPa) (+P)
520
R p0.2 0.2% proof strength (MPa) (+P)
520
+P
Rm - Tensile strength (MPa) (+P)
800-950
Hardness
+A Soft annealed +AC Annealed to achieve spheroidization of the carbides +AR As rolled +AT Solution annealed +C Cold drawn / hard +CR Cold rolled +FP Treated to ferrite-pearlite structure and hardness range +I Isothermal annealing +LC Cold drawn / soft +M Thermo mechanical rolling +N Normalized +NT Normalized and tempered
+P Precipitation hardened +PE Peeled +QA Air quenched and tempered +QL Liquid quenched and tempered +QT Quenched and tempered +S Treated to improve shearability +SH As rolled and turned +SR Cold drawn and stress relieved +T Tempered +TH Treated to hardness range +WW Warm worked +U Untreated
Brinell hardness (HB): (+S)
255
Other
Z - Reduction in cross section on fracture (%) (+P)
25
Registered Designations & Aliases
1.130338MnVS6
Standards
EN 10267 EN 10267: 1998 Ferritic-pearlitic steels for precipitation hardening from hot-working temperatures