UNS C63600 Aluminum-Silicon Bronze
Bronze
O61 (annealed)
Property Overview
Density8.6g/cm³
Elastic Modulus110GPa
Tensile Strength410MPa
Yield Strength150MPa
Brinell HardnessUnknown
Maximum Service Temperature210°C
Chemical Composition
NI
0 to 0.15%
SI
0.7 to 1.3%
CU
93 to 96.3%
AL
3.0 to 4.0%
AS
0 to 0.15%
PB
0 to 0.050%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
SN
0 to 0.2%
ZN
0 to 0.5%
FE
0 to 0.15%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
66 %
Poisson's Ratio
0.34
Shear Modulus
42 GPa
Shear Strength
320 MPa
Tensile Strength: Ultimate (UTS)
410 MPa
Tensile Strength: Yield (Proof)
150 MPa
Physical
Density
8.6 g/cm 3
Thermal
Latent Heat of Fusion
230 J/g
Maximum Temperature: Mechanical
210 °C
Melting Completion (Liquidus)
1030 °C
Melting Onset (Solidus)
980 °C
Specific Heat Capacity
410 J/kg-K
Thermal Conductivity
57 W/m-K
Thermal Diffusivity
16 mm 2 /s
Thermal Expansion
17 µm/m-K
Thermal Shock Resistance
15 points
Electrical
Electrical Conductivity: Equal Volume
12 % IACS
Electrical Conductivity: Equal Weight (Specific)
13 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
210 MJ/m 3
Resilience: Unit (Modulus of Resilience)
100 kJ/m 3
Stiffness to Weight: Axial
7.3 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
13 points
Strength to Weight: Bending
14 points
Environmental
Base Metal Price
30 % relative
Embodied Carbon
2.8 kg CO 2 /kg material
Embodied Energy
45 MJ/kg
Embodied Energy
45 MJ/kg 20 x 10 3 BTU/lb
Embodied Water
340 L/kg
Embodied Water
340 L/kg 40 gal/lb
Registered Designations & Aliases
C63600UNS C63600 Aluminum-Silicon Bronze