C60R
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength710MPa
Yield Strength630MPa
Brinell Hardness241HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 5,65 √ So (%) (+N)
10
A - Min. elongation Lo = 5,65 √ So (%) (+N)
11
A - Min. elongation at fracture (%) (+C)
5
A - Min. elongation at fracture (%) (+C)
6
R p0.2 0.2% proof strength (MPa) (+C)
630
R p0.2 0.2% proof strength (MPa) (+C)
550
R p0.2 0.2% proof strength (MPa) (+C)
480
R p0.2 0.2% proof strength (MPa) (+C)
630
+C
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
380
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
340
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
310
Rm - Tensile strength (MPa) (+C)
800-1150
Rm - Tensile strength (MPa) (+C)
780-1130
Rm - Tensile strength (MPa) (+C)
730-1100
Rm - Tensile strength (MPa) (+N)
710
Rm - Tensile strength (MPa) (+N)
670
Rm - Tensile strength (MPa) (+N)
650
Hardness
Brinell hardness (HBW): (+A)
241
Brinell hardness (HBW): (+S)
255
Brinell hardness (HBW): (+SH)
198 - 278
Other
Nominal thickness (mm):
to 16
Nominal thickness (mm):
16 - 100
Nominal thickness (mm):
100 - 250
Nominal thickness (mm):
5 - 10
Nominal thickness (mm):
10 - 16
Nominal thickness (mm):
16 - 40
Registered Designations & Aliases
1.1223C60R
Standards
EN 10083-2 EN 10083-2: 2006 Steels for quenching and tempering. Technical delivery conditions for non alloy steels
EN 10277-5 EN 10277-5: 2008 Bright steel products. Technical delivery conditions. Steels for quenching and tempering