C16R
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength520-820MPa
Yield Strength400MPa
Brinell Hardness156HB
Maximum Service TemperatureUnknown
Chemical Composition
C
Non alloy special steel Chemical composition of steel C16R (1.1208), Standards of steel C16R (1.1208) Mechanical Properties of steel C16R (1.1208) steel C16R (1.1208) Tensile Strength, Elongation, Proof strength , Hardness%
Mechanical
A - Min. elongation at fracture (%) (+C)
7
A - Min. elongation at fracture (%) (+C)
8
A - Min. elongation at fracture (%) (+C)
9
A - Min. elongation at fracture (%) (+C)
11
A - Min. elongation at fracture (%) (+C)
12
R p0.2 0.2% proof strength (MPa) (+C)
400
R p0.2 0.2% proof strength (MPa) (+C)
360
R p0.2 0.2% proof strength (MPa) (+C)
300
R p0.2 0.2% proof strength (MPa) (+C)
260
R p0.2 0.2% proof strength (MPa) (+C)
235
R p0.2 0.2% proof strength (MPa) (+C)
400
+C
Rm - Tensile strength (MPa) (+C)
520-820
Rm - Tensile strength (MPa) (+C)
500-800
Rm - Tensile strength (MPa) (+C)
450-750
Rm - Tensile strength (MPa) (+C)
400-690
Rm - Tensile strength (MPa) (+C)
360-620
Rm - Tensile strength (MPa) (+SH)
350-620
Hardness
+A Soft annealed +AC Annealed to achieve spheroidization of the carbides +AR As rolled +AT Solution annealed +C Cold drawn / hard +CR Cold rolled +FP Treated to ferrite-pearlite structure and hardness range +I Isothermal annealing +LC Cold drawn / soft +M Thermo mechanical rolling +N Normalized +NT Normalized and tempered
+P Precipitation hardened +PE Peeled +QA Air quenched and tempered +QL Liquid quenched and tempered +QT Quenched and tempered +S Treated to improve shearability +SH As rolled and turned +SR Cold drawn and stress relieved +T Tempered +TH Treated to hardness range +WW Warm worked +U Untreated
Brinell hardness (HBW): (+A)
156
Brinell hardness (HBW): (+N)
100 - 155
Brinell hardness (HBW): (+SH)
105 - 184
Other
Nominal thickness (mm):
5 - 10
Nominal thickness (mm):
10 - 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 63
Nominal thickness (mm):
63 - 100
Registered Designations & Aliases
1.1208C16R
Standards
EN 10084 EN 10084: 2008 Case hardening steels. Technical delivery conditions
EN 10277-4 EN 10277-4: 2008 Bright steel products. Technical delivery conditions. Case hardening steels